Condition for sintering of a newly lined furnace with neutral ramming mass

1. Add ferronickel or top crops and back end crops to the bottom of the furnace, (the center must be flattened), sintering can be started when the furnace is half full.

2. When sintering, the voltage should start from 100kw. After half an hour of operation, the voltage can be pulled to about 250kw. At the same time, it is necessary to constantly observe whether the forma is cut off due to excessive voltage and the furnace is bulged. If one of them occurs, The voltage should be lowered immediately, and the scrape in the furnace should be red before pouring in molten steel.(It is recommended that the furnace be sintered for no less than 3 hours)

3. The temperature of the molten steel should not be lower than 1600 ℃. After the molten steel is filled, the voltage should be pulled to 800kw. The voltage should be pulled up by 100kw to 150kw every 10 minutes till the temperature reaches 1720 ℃. The holding time should be no less than two hours. (During the heat preservation period, the voltage should be reduced to 500kw. The temperature should be measured once every half hour, and the temperature should be slightly raised when it is lower than 1690 ℃. If it is higher than 1710 ℃, go straight to tapping). When the furnace is started cold, it is necessary to check whether there are any cracks in the furnace. If there is, it is necessary to inform the furnace repairer. After the repair is completed, the voltage of the furnace should be pulled to 200kw, and after half an hour of preheating, slowly pull up the voltage at the rate of 200kw in each half hour, it cannot be operated blindly. Otherwise, foreign substance will go into the cracks, causing penetration of molten steel. When the furnace is in normal operation, it is necessary to observe whether the furnace is leaking ramming mass. Whenever the molten steel is tapped out, it is necessary to see if there is any problem in the furnace to carry out the operation of the furnace to ensure the normal production of the furnace.

Note: To prevent thermal damage and mechanical damage, it is important to use the specified type and size of ramming mass for sintering. Medium-sized, densely packed, mild chemical properties aggregates should be used, and care should be taken when feeding. As the melting progresses, the feed should be periodically applied.

Wanhao is a manufacturer who is specialized in designing various kinds of furnace and making refractory products for electric furnace, ladle, tundish, blast furnace, AOD furnace, IF furnace, etc.

Article Source:Condition for sintering of a newly lined furnace with neutral ramming mass
Company name:Wanhao Refractory
Email:sales100@wanhaorefractory.com
Website: http://www.wanhaorefractory.com/

评论

发表评论

此博客中的热门博文

Advantages and disadvantages of fire clay brick

图片
According to production process, fire clay brick is divided into machine made brick and handmade brick. According to structures, fire clay brick is divided into solid brick and hollow brick, and hollow brick can be divided into load-bearing brick and nonbearing brick. Fire clay brick is made at different shapes according to different using requirements. Advantages of fire clay brick： 1. Fire clay brick is environmentally friendly and belongs to resource recycling bricks, so we can rest assured use fire clay brick. Fire clay bricks won’t be harmful to our health. 2.Fire clay brick has advantages of fireproof and heat insulation. Used clay brick can be used as concrete so that to save a lot of resources. 3.The price of fire clay brick is not as expensive as that of other fire bricks. Light weight brick is more expensive than fire clay brick. Besides, fire clay brick is very cheap and very durable 4. Fire clay brick has good moisture-proof function, it also has the a...
阅读全文

Installation of ladle slide gate and nozzle

图片
1.Before installing the upper steel ladle, first check the use of the water block brick. When the pit or crack occurs, use the repair refractory material to repair it, and then proceed to the next step. 2. Take the water pipe test, check the gap between the nozzle brick and the brick and the positioning of the nozzle brick. It is forbidden to manually remove the head of the water inlet and install it. 3. After checking the appropriate, remove the nozzle brick and apply refractory mud evenly on the outer wall of the upper nozzle brick. The thickness of the refractory mud is controlled at about 10mm (according to the actual clearance). When the gap between the nozzle and the brick is large, the asbestos cloth can be used. The head of the nozzle is evenly wound separately. 4. When installing the water inlet, the nozzle brick should be smoothly fed into the brick. During operation, avoid the gap in the lower part of the nozzle brick. 5. The water inlet must be re...
阅读全文

Blast furnace accident: six reasons for the freezing of the hearth

图片
1. The furnace is out of order. In many cases, the blast furnace condition is abnormal due to poor quality of the raw fuel or improper basic operating system. 2. Operational errors The prelude to the freezing of the hearth is the furnace cool. It is normal for the blast furnace temperature to fluctuate within a certain range, and the cool furnace that causes the hearth to freeze is often caused by improper operation. 3.A large amount of cooling water leaks into the hearth. 4. Long-term rest or sealing furnace Long-term rest is a common cause of freezing of the hearth even if there is no water leakage from the cooling equipment. 5. Equipment accident If the test is not enough before the start of the furnace, it will often cause equipment accidents. 6. The quality of raw fuel deteriorates. Wanhao is a manufacturer who is specialized in designing various kinds of furnace and making refractory products for electric furnace, ladle, tundish, bla...
阅读全文