The different of HP graphite electrode and UHP graphite electrode

Ultra-high power graphite electrodes refer to graphite electrodes that allow the use of current densities greater than 25 A / cm2. UHP graphite electrode is mainly used in ultra-high power electric furnace and ladle furnace.
High power graphite electrodes refer to the graphite electrode that allows the use of a current density of 18 ~ 25A / cm2.Graphite electrode has good electrical properties and chemical stability. What’s more, graphite electrode has advantages of high mechanical strength, low impurity content and good vibration resistance. Graphite electrodes are good conductors of heat and electricity.
HP graphite electrode is widely used in steelmaking electric furnace, refining furnaces, production of ferroalloy, industrial silicon, yellow phosphorus, corundum , submerged arc furnaces and other smelting furnaces that produce high temperatures by electric arc.
1.
RP graphite electrode Specification :
Bulk Density : >1.52g/cm3
Specific Resistance : <9.0 Micro Ohm/m
Bending Strength : >7.8 MPa
Young's Modulus : <9.3 GPa
Ash : 0.50% (max)
C.T.E : <2.9 x 10 -6/C
Specification of Nipples:
Bulk Density : >1.68g/cm3
Specific Resistance : <8.5 Micro Ohm/m
Bending Strength : >13.00 MPa
Elastic Modulus : <14.00 GPa
Ash : 0.50% (max)
C.T.E : <2.90 x 10 -6/C (max)
Nipple Thread : 3TPI or 4TPI
2.
HP graphite electrode Specification :
Bulk Density : >1.6g/cm3
Specific Resistance : <7.2 Micro Ohm/m
Bending Strength : >10.5 MPa
Young's Modulus : <12.00 GPa
Ash : 0.30% (max)
C.T.E : <2.4 x 10 -6/C
Specification of Nipples:
Bulk Density : >1.7g/cm3
Specific Resistance : <6.5 Micro Ohm/m
Bending Strength : >14.00 MPa
Elastic Modulus : <16.00 GPa
Ash : 0.30% (max)
C.T.E : <2.20 x 10 -6/C (max)
Nipple Thread : 3TPI or 4TPI
3.
UHP graphite electrode Specification :
Bulk Density : >1.68g/cm3
Specific Resistance : <5.8 Micro Ohm/m
Bending Strength : >18.3 MPa
Young's Modulus : <12.00 GPa
Ash : 0.30% (max)
C.T.E : 1.5 x 10 -6/C
Specification of Nipples:
Bulk Density : >1.78g/cm3
Specific Resistance : <4.3 Micro Ohm/m
Bending Strength : >20.70 MPa
Elastic Modulus : <19.00 GPa
Ash : 0.30% (max)
C.T.E : 1.40 x 10 -6/C (max)
Nipple Thread : 3TPI or 4TPI
This is HP Graphite Electrode. Wanhao refractory offers best HP Graphite Electrode with cheap price. If you need it, please contact me anytime. My email is sales100@wanhaorefractory.com. Welcome to view our web to know more details about HP Graphite Electrode. There have many kinds of refractory products for you.
Article Source: HP Graphite electrode
Company name: Wanhao Refractory
Email:sales100@wanhaorefractory.com
Website:http://www.wanhaorefractory.com/
HP Graphite Electrode

评论

发表评论

此博客中的热门博文

Advantages and disadvantages of fire clay brick

图片
According to production process, fire clay brick is divided into machine made brick and handmade brick. According to structures, fire clay brick is divided into solid brick and hollow brick, and hollow brick can be divided into load-bearing brick and nonbearing brick. Fire clay brick is made at different shapes according to different using requirements. Advantages of fire clay brick： 1. Fire clay brick is environmentally friendly and belongs to resource recycling bricks, so we can rest assured use fire clay brick. Fire clay bricks won’t be harmful to our health. 2.Fire clay brick has advantages of fireproof and heat insulation. Used clay brick can be used as concrete so that to save a lot of resources. 3.The price of fire clay brick is not as expensive as that of other fire bricks. Light weight brick is more expensive than fire clay brick. Besides, fire clay brick is very cheap and very durable 4. Fire clay brick has good moisture-proof function, it also has the a...
阅读全文

The application of carburants

图片
Carburants are for casting iron. Carburants are added to steel, iron and carbon by carbon raw materials. High-quality carbon agent is essential for the production of high-quality steel auxiliary additives. At present, the vast majority of carburants are suitable for electric furnace smelting. Electric furnace smelting of the feeding method, the carbon agent should be with the scrap and other materials into the inside together, the addition of small doses can be added to the surface of the molten iron. But to avoid large quantities of molten iron to feed, to prevent excessive oxidation and the effect of carbon is not obvious and the cast carbon content is not enough. The amount of carbon agent added, according to the ratio of other raw materials and carbon content to set. Features 1.Absorption rate of it is up to 90% or more. 2.Improve the graphite form, increase the number of graphite, fine graphite, improve product mechanical properties, improve pro...
阅读全文

Installation of ladle slide gate and nozzle

图片
1.Before installing the upper steel ladle, first check the use of the water block brick. When the pit or crack occurs, use the repair refractory material to repair it, and then proceed to the next step. 2. Take the water pipe test, check the gap between the nozzle brick and the brick and the positioning of the nozzle brick. It is forbidden to manually remove the head of the water inlet and install it. 3. After checking the appropriate, remove the nozzle brick and apply refractory mud evenly on the outer wall of the upper nozzle brick. The thickness of the refractory mud is controlled at about 10mm (according to the actual clearance). When the gap between the nozzle and the brick is large, the asbestos cloth can be used. The head of the nozzle is evenly wound separately. 4. When installing the water inlet, the nozzle brick should be smoothly fed into the brick. During operation, avoid the gap in the lower part of the nozzle brick. 5. The water inlet must be re...
阅读全文