Specifications of magnesia calcium bricks

The magnesia-calcium brick, also known as high calcium magnesite brick, is a kind of magnesial refractory material with periclase as principal crystalline phase and tricalcium silicate as secondary phase. It contains 80 % ~ 87% MgO, 6 % ~ 9% CaO, CaO/SiO2 ratio is between 2.2 ~ 3.0. Its significant structural feature is periclase directly contact with dicalcium silicate and tricalcium silicate, making eutectic solution-4 Cao·Al2O3·Fe2O3 fill into crystal gap between dicalcium silicate and tricalcium silicate. Its porosity is low, the refractoriness under load is higher than 1700 ℃. It has good alkaline slag resistance ability, but with poor thermal shock resistance.
Made by calcium magnesia sand as refractory raw material , it will be made by firing at 1550~1600 ℃ after crushing, burdening, mixing and molding. It will be used at eye place of side-blown converter, top place of open-hearth furnace and oxygen-blown converter etc.


Magnesia-calcium brick has seven properties: High temperature resistance, slag resistance, spalling resistance, wear resistance, purifying molten steel and hydration resistance performance.


With the increasing production of stainless steel and all kinds of clean steel refractory products, the demand of various magnesia calcium brick are increasing accordingly. For better production and using correctly, detailed understanding and learning of working performance and influencing factors of magnesia calcium bricks are very necessary.

Article Source:  Specifications of magnesia calcium bricks

Company name: Wanhao Refractory
Email: sales100@wanhaorefractory.com
Website: http://www.wanhaorefractory.com/




评论

发表评论

此博客中的热门博文

Advantages and disadvantages of fire clay brick

图片
According to production process, fire clay brick is divided into machine made brick and handmade brick. According to structures, fire clay brick is divided into solid brick and hollow brick, and hollow brick can be divided into load-bearing brick and nonbearing brick. Fire clay brick is made at different shapes according to different using requirements. Advantages of fire clay brick： 1. Fire clay brick is environmentally friendly and belongs to resource recycling bricks, so we can rest assured use fire clay brick. Fire clay bricks won’t be harmful to our health. 2.Fire clay brick has advantages of fireproof and heat insulation. Used clay brick can be used as concrete so that to save a lot of resources. 3.The price of fire clay brick is not as expensive as that of other fire bricks. Light weight brick is more expensive than fire clay brick. Besides, fire clay brick is very cheap and very durable 4. Fire clay brick has good moisture-proof function, it also has the a...
阅读全文

The application of carburants

图片
Carburants are for casting iron. Carburants are added to steel, iron and carbon by carbon raw materials. High-quality carbon agent is essential for the production of high-quality steel auxiliary additives. At present, the vast majority of carburants are suitable for electric furnace smelting. Electric furnace smelting of the feeding method, the carbon agent should be with the scrap and other materials into the inside together, the addition of small doses can be added to the surface of the molten iron. But to avoid large quantities of molten iron to feed, to prevent excessive oxidation and the effect of carbon is not obvious and the cast carbon content is not enough. The amount of carbon agent added, according to the ratio of other raw materials and carbon content to set. Features 1.Absorption rate of it is up to 90% or more. 2.Improve the graphite form, increase the number of graphite, fine graphite, improve product mechanical properties, improve pro...
阅读全文

Installation of ladle slide gate and nozzle

图片
1.Before installing the upper steel ladle, first check the use of the water block brick. When the pit or crack occurs, use the repair refractory material to repair it, and then proceed to the next step. 2. Take the water pipe test, check the gap between the nozzle brick and the brick and the positioning of the nozzle brick. It is forbidden to manually remove the head of the water inlet and install it. 3. After checking the appropriate, remove the nozzle brick and apply refractory mud evenly on the outer wall of the upper nozzle brick. The thickness of the refractory mud is controlled at about 10mm (according to the actual clearance). When the gap between the nozzle and the brick is large, the asbestos cloth can be used. The head of the nozzle is evenly wound separately. 4. When installing the water inlet, the nozzle brick should be smoothly fed into the brick. During operation, avoid the gap in the lower part of the nozzle brick. 5. The water inlet must be re...
阅读全文