The application of carburants

Carburants are for casting iron. Carburants are added to steel, iron and carbon by carbon raw materials. High-quality carbon agent is essential for the production of high-quality steel auxiliary additives.
At present, the vast majority of carburants are suitable for electric furnace smelting. Electric furnace smelting of the feeding method, the carbon agent should be with the scrap and other materials into the inside together, the addition of small doses can be added to the surface of the molten iron. But to avoid large quantities of molten iron to feed, to prevent excessive oxidation and the effect of carbon is not obvious and the cast carbon content is not enough. The amount of carbon agent added, according to the ratio of other raw materials and carbon content to set.
Features
1.Absorption rate of it is up to 90% or more.
2.Improve the graphite form, increase the number of graphite, fine graphite, improve product mechanical properties, improve processing performance.
Instructions
1. Ingredients according to the molten steel (iron) water carbon content requirements to adjust the amount of carbon agent added, with the metal charge into the central part of the furnace, the carbon absorption rate of up to 90-99%.
2. After the molten steel (iron) melts, the trace amount of carbon can be added to the surface of the steel (iron) water. The iron (iron) water is agitated by the eddy current of the steel (iron) to dissolve and absorb the carbon, and the carbon absorption is 80-95 %.
Precautions
Do not melt the carbon agent does not carry out slag operation, to prevent the carbon agent wrapped in waste residue inside, affecting the absorption of carbon agent.

Article Source:  The application of carburants
Company name: Luoyang Wanhao New Material Co., Ltd
Email:sales100@wanhaorefractory.com
Website:http://www.wanhaorefractory.com/ 



评论

发表评论

此博客中的热门博文

Advantages and disadvantages of fire clay brick

图片
According to production process, fire clay brick is divided into machine made brick and handmade brick. According to structures, fire clay brick is divided into solid brick and hollow brick, and hollow brick can be divided into load-bearing brick and nonbearing brick. Fire clay brick is made at different shapes according to different using requirements. Advantages of fire clay brick： 1. Fire clay brick is environmentally friendly and belongs to resource recycling bricks, so we can rest assured use fire clay brick. Fire clay bricks won’t be harmful to our health. 2.Fire clay brick has advantages of fireproof and heat insulation. Used clay brick can be used as concrete so that to save a lot of resources. 3.The price of fire clay brick is not as expensive as that of other fire bricks. Light weight brick is more expensive than fire clay brick. Besides, fire clay brick is very cheap and very durable 4. Fire clay brick has good moisture-proof function, it also has the a
阅读全文

Brief introduction of gunning material

  The EAF gunning material bears the same high temperature and harsh working environment as the repaired furnace lining during the smelting process. Therefore, in addition to high refractoriness, erosion resistance, erosion resistance, spalling resistance, etc., the EAF gunning mix must also be compatible with the repaired furnace lining. The lining has good adhesion. The gunning materials for electric furnaces include magnesia, magnesia-dolomite, magnesia-chromite, magnesia-carbon, magnesia-dolomite-carbon, etc., and some highly active seawater magnesia are used in the aggregate. To promote sintering and improve the density and strength of the gunning layer. In order to make the gunning material solidify quickly during the gunning operation and attach to the furnace lining at the same time, a small amount of additives are often added to the aggregate. 1.When adding Al, Mg and other low melting point metal powders for gunning, the oxidation heat of metal powder helps
阅读全文