The different of HP graphite electrode and UHP graphite electrode

Ultra-high power graphite electrodes refer to graphite electrodes that allow the use of current densities greater than 25 A / cm2. UHP graphite electrode is mainly used in ultra-high power electric furnace and ladle furnace.
High power graphite electrodes refer to the graphite electrode that allows the use of a current density of 18 ~ 25A / cm2.Graphite electrode has good electrical properties and chemical stability. What’s more, graphite electrode has advantages of high mechanical strength, low impurity content and good vibration resistance. Graphite electrodes are good conductors of heat and electricity.
HP graphite electrode is widely used in steelmaking electric furnace, refining furnaces, production of ferroalloy, industrial silicon, yellow phosphorus, corundum , submerged arc furnaces and other smelting furnaces that produce high temperatures by electric arc.
1.
RP graphite electrode Specification :
Bulk Density : >1.52g/cm3
Specific Resistance : <9.0 Micro Ohm/m
Bending Strength : >7.8 MPa
Young's Modulus : <9.3 GPa
Ash : 0.50% (max)
C.T.E : <2.9 x 10 -6/C
Specification of Nipples:
Bulk Density : >1.68g/cm3
Specific Resistance : <8.5 Micro Ohm/m
Bending Strength : >13.00 MPa
Elastic Modulus : <14.00 GPa
Ash : 0.50% (max)
C.T.E : <2.90 x 10 -6/C (max)
Nipple Thread : 3TPI or 4TPI
2.
HP graphite electrode Specification :
Bulk Density : >1.6g/cm3
Specific Resistance : <7.2 Micro Ohm/m
Bending Strength : >10.5 MPa
Young's Modulus : <12.00 GPa
Ash : 0.30% (max)
C.T.E : <2.4 x 10 -6/C
Specification of Nipples:
Bulk Density : >1.7g/cm3
Specific Resistance : <6.5 Micro Ohm/m
Bending Strength : >14.00 MPa
Elastic Modulus : <16.00 GPa
Ash : 0.30% (max)
C.T.E : <2.20 x 10 -6/C (max)
Nipple Thread : 3TPI or 4TPI
3.
UHP graphite electrode Specification :
Bulk Density : >1.68g/cm3
Specific Resistance : <5.8 Micro Ohm/m
Bending Strength : >18.3 MPa
Young's Modulus : <12.00 GPa
Ash : 0.30% (max)
C.T.E : 1.5 x 10 -6/C
Specification of Nipples:
Bulk Density : >1.78g/cm3
Specific Resistance : <4.3 Micro Ohm/m
Bending Strength : >20.70 MPa
Elastic Modulus : <19.00 GPa
Ash : 0.30% (max)
C.T.E : 1.40 x 10 -6/C (max)
Nipple Thread : 3TPI or 4TPI
This is HP Graphite Electrode. Wanhao refractory offers best HP Graphite Electrode with cheap price. If you need it, please contact me anytime. My email is sales100@wanhaorefractory.com. Welcome to view our web to know more details about HP Graphite Electrode. There have many kinds of refractory products for you.
Article Source: HP Graphite electrode
Company name: Wanhao Refractory
Email:sales100@wanhaorefractory.com
Website:http://www.wanhaorefractory.com/
HP Graphite Electrode

评论

发表评论

此博客中的热门博文

Advantages and disadvantages of fire clay brick

图片
According to production process, fire clay brick is divided into machine made brick and handmade brick. According to structures, fire clay brick is divided into solid brick and hollow brick, and hollow brick can be divided into load-bearing brick and nonbearing brick. Fire clay brick is made at different shapes according to different using requirements. Advantages of fire clay brick： 1. Fire clay brick is environmentally friendly and belongs to resource recycling bricks, so we can rest assured use fire clay brick. Fire clay bricks won’t be harmful to our health. 2.Fire clay brick has advantages of fireproof and heat insulation. Used clay brick can be used as concrete so that to save a lot of resources. 3.The price of fire clay brick is not as expensive as that of other fire bricks. Light weight brick is more expensive than fire clay brick. Besides, fire clay brick is very cheap and very durable 4. Fire clay brick has good moisture-proof function, it also has the a
阅读全文

Introduction and selection of burner bricks

图片
  Burner brick is a kind of refractory brick used with the burner of high temperature kiln, such as blast furnace gas burner, special burner for lime furnace kiln, shaft furnace burner, regenerative heating furnace burner, etc. The shapes are different, and the burner bricks used do not have fixed specifications and sizes, and they often need to be customized in refractory manufacturers. The use of high-aluminum steel fiber castables can meet the working conditions of most burners. The function of the burner brick is: 1.The fuel is heated to the ignition temperature in the burner brick, so that it is easy to ignite and burn quickly. 2.Keep a certain high temperature in the burner brick to stabilize the combustion process and avoid pulsation or fuel interruption. 3.The flame shape of the organization meets the requirements of the heating process. 4.To further mix the fuel and air. Therefore, the burner brick is an indispensable high-temperature resistant material for the
阅读全文

The application of carburants

图片
Carburants are for casting iron. Carburants are added to steel, iron and carbon by carbon raw materials. High-quality carbon agent is essential for the production of high-quality steel auxiliary additives. At present, the vast majority of carburants are suitable for electric furnace smelting. Electric furnace smelting of the feeding method, the carbon agent should be with the scrap and other materials into the inside together, the addition of small doses can be added to the surface of the molten iron. But to avoid large quantities of molten iron to feed, to prevent excessive oxidation and the effect of carbon is not obvious and the cast carbon content is not enough. The amount of carbon agent added, according to the ratio of other raw materials and carbon content to set. Features 1.Absorption rate of it is up to 90% or more. 2.Improve the graphite form, increase the number of graphite, fine graphite, improve product mechanical properties, improve pro
阅读全文